Design Komposisi Beton Untuk Panel Beton Menggunakan Bahan Tambah Serat Fiberglass

Penulis

  • Surya Laksa Andanu Sekolah Tinggi Teknologi Dumai
  • Aidil Abrar Sekolah Tinggi Teknologi Dumai
  • Sony Adiya Putra Sekolah Tinggi Teknologi Dumai
  • Welly Desriyati Sekolah Tinggi Teknologi Dumai

DOI:

https://doi.org/10.52072/slumptes.v2i2.714

Kata Kunci:

Fiber concrete, normal concrete, Fiberglass

Abstrak

To overcome the problem of deficiencies in concrete, there are various ways, one of which is the innovation of mixing concrete with fiber which is an innovation to increase the compressive strength of concrete. Fiber concrete is a composite material in which fiber is added to the concrete mixture. The fiber used in this research is Fiberglass. Comparison results of the compressive strength of normal concrete and Fiberglass fiber. Normal concrete aged 7 days has an average compressive strength of 107.76 Kg/Cm2, aged 14 days the average compressive strength is 154.09 Kg/cm2, aged 28 days the average compressive strength is 166.17 Kg/cm2. And for concrete with added 3% Fiberglass fiber, aged 7 days, the average compressive strength is 117.83 Kg/cm2, aged 14 days, the average compressive strength is 148.05 Kg/cm2, aged 28 days, the average compressive strength is 164, 66 Kg/cm2. for concrete with 5% Fiberglass fiber added at age 7 the average compressive strength is 123.87 Kg/cm2, at 14 days the average compressive strength is 146.53 Kg/cm2, at 28 days the average compressive strength is 187.32 Kg/cm2. for concrete with added 9% Fiberglass fiber, aged 7 days, the average compressive strength is 99.70 Kg/cm2, aged 14 days, the average compressive strength is 128.41 Kg/cm2, aged 28 days, the average compressive strength is 149.56 Kg/cm2.

Unduhan

Data unduhan belum tersedia.

Referensi

ASTM. (2001). Standard Specification for Chemical Admixtures for Concrete 1. C 494, 4, 1-9.

Badan Standardisasi Nasional. (1991). SNI 03-2495-1991: Spesifikasi Bahan Tambahan Untuk Beton.

Badan Standardisasi Nasional. (2000). SNI 03-2834-2000: Tata Cara Pembuatan Rencana Campuran Beton Normal

Badan Standardisasi Nasional. (2011). SNI 2493-2011: Tata Cara Pembuatan dan Perawatan Benda Uji Beton di Laboratorium.

Badan Standardisasi Nasional. (2013). SNI 2847-2013: Persyaratan Beton Struktural untuk Bangunan Gedung.

Indonesia, S. N., & Nasional, B. S (2000). Tata Cara Pembuatan Rencana Campuran Beton Normal.

Indonesia, S. N., & Nasional, B. S (2015). Semen Portland.

Jemima. (2017). Pengaruh Nilai Kuat Tekan Beton EPS Dengan Penggunaan Fiberglass Dan Perawatan Curing Dan Non Curing.

Kusuma, G. H., Kole, P., & Segel, R. (1994). Pedoman Pengerjaan Beton. Jakarta: Erlangga.

Le, H. T., Muller, M., Siewert, K., & Ludwig, H. M. (2015). The Mix Design For Self-Compacting High Performance Concrete Containing Various Mineral Admixtures. Materials and Design, 51-62.

Mariani, Sampebulu, V., & Ahmad, A. G. (2009). Pengaruh Penambahan Admixture Terhadap Karakteristik Self Compacting Concrete (SCC). SMARTek, (6)12.

Mustari, M. I. (2011). Studi Kuat Lentur Beton Pada Perkerasan Kaku Dengan Penambahan Serat Fiberglass Pada Beton Normal. ILTEK, (6)12, 866-870.

Peraturan Beton Indonesia (1971). Penjelasan & Pembahasan mengenai Peraturan Beton Indonesia 1971.

Safarizki, H. A. (2017). Pengaruh Bahan Tambah Serbuk Bata dan Serat Fiber Pada Self Compacting Concrete (SCC). Jurnal Ilmiah Teknosains, 3(02).

Satria. (2015). Pengaruh Penggunaan Fiber Glass Pada Beton Ringan Terhadap Kuat Tekan Dan Kuat Lentur. Universitas Atma Jaya Yogyakarta.

Sianipar, Y. K. P. (2021). Pengaruh Penambahan Serat Fiberglass Dan Substitusi Fly Ash Terhadap Pengujian Self Compacting Concrete.

Tjokrodimuljo, K. (1992). Teknologi Beton, Biro Penerbit, Yogyakarta.

Universitas Islam Indonesia, 2016, Buku Panduan Praktikum Teknologi Bahan Konstruksi, Yogyakarta.

Wang, C.K. dan Salmon, C.G., 1990, Desain Beton Bertulang, Terjemahan oleh Binsar Hariandja, Erlangga, Jakarta.

##submission.downloads##

Diterbitkan

2024-01-15